The effect of glass ionomer containing various levels of titanium dioxide nanoparticles against Streptococcus mutans

Fatemeh Esmi; Atefeh Saffari; Seyed Mahmood Amin Marashi; Parinaz Emam Verdi

Annals of Military and Health Sciences Research

Current Issue All Issues In Press Accepted Manuscripts Search

Journal Information Editors and Boards Indexing and Listing Sources Reviewer and AE Registration Form Journal Metrics Open Peer Review (OPR)Publication Ethics and Malpractice Statement Contact Us Support

Authors Guide Submit Manuscript

The effect of glass ionomer containing various levels of titanium dioxide nanoparticles against Streptococcus mutans

Author(s):

Fatemeh Esmi¹,

Atefeh Saffari¹,

Seyed Mahmood Amin Marashi²,

Parinaz Emam Verdi^3,*

1Assistant professor, Dental Research Center, Dental school, Babol University of Medical Sciences, Babol, Iran, Andorra

2Assistant professor, Microbiology Department, Babol University of Medical Sciences, Babol, Iran, Andorra

3Dental student Dental Research Center, Dental school, Babol University of Medical Sciences, Babol, Iran, Andorra

Annals of Military and Health Sciences Research:Vol. 11, issue 1; e66788

Published online:Feb 07, 2013

Article type:Research Article

Received:Oct 24, 2012

Accepted:Jan 07, 2013

How to Cite:Fatemeh EsmiAtefeh SaffariSeyed Mahmood Amin MarashiParinaz Emam VerdiThe effect of glass ionomer containing various levels of titanium dioxide nanoparticles against Streptococcus mutans.Ann Mil Health Sci Res.11(1):e66788.

Abstract

Background: The use of nanoparticles in improvement antibacterial property of dental resins is one of the most important issues in recent studies. Studies which added these particles to resin materials have reported desirable results in decreasing bacteria’s growth. Titanium dioxide nanoparticles have been proposed for reinforcing fillers in dental resin composites and epoxy. The aim of this study was to evaluate the effect of adding titanium dioxide nanoparticles into a light cure glass ionomer on antibacterial properties of this resin against streptococcus mutans.

Materials and Methods: In this in-vitro study, samples were divided into 5 light cure glass ionomergroups which contain respectively of 0 (as control group), o.5, 1, 3, 5 weight percentage of nano-titanium dioxide. 15 discs (3 from each experimental group) were cured in plastic frames with 2mm thickness and 8mm diameter, for disc diffusion test. Then antibacterial properties against streptococcus mutans were studied in chocolate agar culture. For Direct Contact Test, 15 micro-tubes containing resin groups (3 discs from each experimental group) were prepared and their antibacterial effect were evaluated after 3, 6 and 24 hours. The data was analyzed by Kruskal-Wallis Test and Mann-Whitney Test.

Results: In Disc Diffusion Test the amount of antibacterial effect around discs, containing 0.5 nanoparticles was similar to halo around the other discs containing nanoparticles, and it was little more than control group. In Direct Contact Test, glass ionomers containing nanoparticles, number of bacteria was diminished on surface of resin groups that contain more percentages of nanoparticles at 3, 6 24 hours, . Four experimental groups did not reveal any significant difference, but it was diminished in compare to control group.

Conclusions: However the growth of bacteria in both tests in comparison with control group was decreased, antibacterial property of samples that contain nanoparticles doesn’t show any significant difference. This property was more significant in direct contact with bacteria.